| About |
|---|
| TECHNYL® ONE J 60X1 V15 black is a high temperature polyamide based on a non-halogenated flame retardant system, reinforced with 15% of glass fiber with best-in-class fire protection behavior, for injection moulding. This product has superior electrical performance compared to traditional high-performance plastics. Its low corrosion ensures processing tools longevity. This product, based on a high fluidity matrix, offers strong benefits in term of productivity and design freedom. The data provided are based on laboratory/experimental results. These data could be adjusted after industrial production.&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA 66/6T |
| Material Status | Commercial: Active |
| Features | Heat Resistance, Good,Corrosion Resistant,Halogen free |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.0 | % | |
| MD | 0.50 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.75 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.7 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 7600 | MPa | |
| tensile strength | |||
| Fracture, 23 ℃ | 125 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.8 | % | |
| Bending modulus | |||
| 23℃ | 6300 | MPa | |
| bending strength | |||
| 23℃ | 120 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 47 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 245 | ℃ | |
| Melting temperature | 278 | ℃ | |
| Relative temperature index | |||
| Electrical performance, 0.75 mm | 150 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 0.8 mm | 35 | kV/mm | |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-0 | ||
| 1.60 mm | |||
| 3.20 mm | |||
| Glowing wire flammability index | |||
| 0.80 mm | 960 | ℃ | |
| 1.6 mm | 960 | ℃ | |
| 3.2 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | |||
| 0.8 mm | 750 | ℃ | |
| 1.6 mm | 725 | ℃ | |
| 3.2 mm | 775 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Injection instructions | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Recommended maximum moisture content | 0.12 | % | |
| Temperature at the rear of the barrel | 285 to 295 | °C | |
| Temperature in the middle of the barrel | 290 to 300 | °C | |
| Front temperature of material barrel | 290 to 300 | °C | |
| Mold temperature | 90 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |