TECHNYL® ONE J 60X1 V30 BLACK

About
TECHNYL® ONE J 60X1 V30 Black is a high temperature polyamide based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber with best-in-class fire protection behavior, for injection moulding. A full yellow card is available with a UL94 V0 rating at 0.4 mm, unmatched thermal ageing properties (150°C electrical RTI – Relative Thermal Index), and outstanding electrical properties, including a high comparative tracking index (CTI 0 for 600 volts and higher). This product has superior electrical performance compared to traditional high-performance plastics. Its low corrosion ensures processing tools longevity. This Technyl is laser welding suitable. This product, based on a high fluidity matrix, offers strong benefits in term of productivity and design freedom.&&

About

TECHNYL® ONE J 60X1 V30 Black is a high temperature polyamide based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber with best-in-class fire protection behavior, for injection moulding. A full yellow card is available with a UL94 V0 rating at 0.4 mm, unmatched thermal ageing properties (150°C electrical RTI – Relative Thermal Index), and outstanding electrical properties, including a high comparative tracking index (CTI 0 for 600 volts and higher). This product has superior electrical performance compared to traditional high-performance plastics. Its low corrosion ensures processing tools longevity. This Technyl is laser welding suitable. This product, based on a high fluidity matrix, offers strong benefits in term of productivity and design freedom.&&

Product Description
Supplier	DOMO
Generic	PA 66/6T
Material Status	Commercial: Active
Features	Halogen free,Laser welding,Arc resistance,High liquidity,Good stripping performance,IR Laser Markable,Corrosion Resistant,Good surface appearance
Availabilitys	Africa & Middle East ,Latin America,Europe,Asia Pacific,North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.41	g/cm³
Water absorption rate
23℃，24hr	0.63	%
Equilibrium, 23 ℃, 50% RH	1.3	%

MECHANICAL	Nominal value	Unit
Tensile modulus
23℃	11000	MPa
tensile strength
Fracture, 23 ℃	145	MPa
Tensile strain
Fracture, 23 ℃	2.5	%
Bending modulus
23℃	9000	MPa
bending strength
23℃	230	MPa

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
-30℃	6.0	kJ/m²
23℃	6.5	kJ/m²
Charpy Unnotch Impact strength
-30℃	50	kJ/m²
23℃	55	kJ/m²
Impact strength of cantilever beam notch
23℃	9.5	kJ/m²
Notched impact strength of cantilever beam
23℃	55	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
0.45 MPa, unannealed	274	℃
1.8 MPa, unannealed	257	℃
Melting temperature	280	℃
Relative temperature index
Electrical performance, 0.40 mm	150	℃

Electrical performance	Nominal value	Unit
Surface resistivity	2.0E+15	ohms
Volume resistivity	1.0E+15	ohms·cm
Dielectric strength
0.8 mm	35	kV/mm
Compared to the leakage tracing index
Solution A	600	V

FLAME CHARACTERISTICS	Nominal value	Unit
Flame retardant level
0.40 mm	V-0
0.80 mm
1.60 mm
3.20 mm
Glowing wire flammability index
0.80 mm	960	℃
1.6 mm	960	℃
3.2 mm	960	℃
Igniting temperature of the hot wire
0.8 mm	800	℃
1.6 mm	800	℃
Extreme oxygen index	45	%

Supplementary information	Nominal value	Unit	Test method
European Railway Certification
R22	HL3
R23	HL3

Process Conditions
Injection	Nominal value	Unit	Test method
Injection instructions	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.12	%
Temperature at the rear of the barrel	285 to 295	°C
Temperature in the middle of the barrel	290 to 300	°C
Front temperature of material barrel	290 to 300	°C
Mold temperature	90 to 110	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.