| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA 66/6T |
| Material Status | Commercial: Active |
| Features | Arc resistance,Good stripping performance,Halogen free,High liquidity,Good surface appearance,Corrosion Resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | |
| Water absorption rate | |||
| 23℃，24hr | 0.55 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.3 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 11000 | MPa | |
| Tensile stress (fracture, 23 ° C) | 130 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.1 | % | |
| Bending modulus | |||
| 23℃ | 9000 | MPa | |
| Bending stress (23 ° C) | 210 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 4.0 | kJ/m² | |
| 23℃ | 5.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 35 | kJ/m² | |
| 23℃ | 45 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 9.5 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| 23℃ | 55 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 260 | ℃ | |
| 1.8 MPa, unannealed | 250 | ℃ | |
| Melting temperature | 280 | ℃ | |
| RTI Elec（0.40 mm） | 150 | °C |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0E+15 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm | |
| Dielectric strength | |||
| 0.8 mm | 35 | kV/mm | |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.40 mm | V-0 | ||
| 0.80 mm | |||
| 1.60 mm | |||
| 3.20 mm | |||
| Glowing wire flammability index | |||
| 0.80 mm | 960 | ℃ | |
| 1.6 mm | 960 | ℃ | |
| 3.2 mm | 960 | ℃ | |
| Hot filament ignition temperature | |||
| 0.8 mm | 800 | °C | |
| 1.6 mm | 800 | °C | |
| Extreme oxygen index | 45 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| European Railway Certification | |||
| R22 | HL3 | ||
| R23 | HL3 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Recommended maximum moisture content | 0.12 | % | |
| Temperature at the rear of the barrel | 285 to 295 | °C | |
| Temperature in the middle of the barrel | 290 to 300 | °C | |
| Front temperature of material barrel | 290 to 300 | °C | |
| Mold temperature | 90 to 110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |