TECHNYL STAR® S 60X1 V30 BLACK 15 N

About
TECHNYL STAR® S 60X1 V30 Black 15N is a grade based on a non-halogenated flame retardant system and on a patented high flow polyamide 6 resin (TechnylStar), reinforced of 30% of glass fiber, heat stabilized, for injection moulding. This grade is Heat stabilized and provides optimized injection moulding performance.&&

Product Description
Supplier	DOMO
Generic	PA6
Material Status	Commercial: Active
Features	Corrosion Resistant,Good surface appearance,High liquidity,Halogen free,Good stripping performance,Arc resistance,low-temperature impact resistance
Availabilitys	Africa & Middle East ,North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.42	g/cm³
Water absorption rate
23℃，24hr	0.87	%
Saturation, 23 ℃	4.0	%
Equilibrium, 23 ℃, 50% RH	1.7	%

MECHANICAL	Nominal value	Unit
Tensile modulus
23℃	10600	MPa
tensile strength
Fracture, 23 ℃	133	MPa
Fracture, 23 ℃	147	MPa
Tensile strain
Fracture, 23 ℃	2.6	%
Fracture, 23 ℃	2.1	%
Bending modulus
23℃	9870	MPa
23℃	9600	MPa
bending strength
23℃	200	MPa
23℃	230	MPa

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
-30℃	8.5	kJ/m²
23℃	9.0	kJ/m²
Charpy Unnotch Impact strength
-30℃	43	kJ/m²
23℃	56	kJ/m²
Impact strength of cantilever beam notch
23℃	90	J/m
23℃	9.0	kJ/m²
Notched impact strength of cantilever beam
23℃	50	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
0.45 MPa, unannealed	205	℃
1.8 MPa, unannealed	205	℃
Melting temperature	222	℃

Electrical performance	Nominal value	Unit
Surface resistivity	6.0E+14	ohms
Volume resistivity	1.0E+15	ohms·cm
Dielectric strength
0.8 mm	38	kV/mm
2 mm	25	kV/mm
Relative permittivity	2.90
Dissipation factor	—
Compared to the leakage tracing index
Solution A	600	V

FLAME CHARACTERISTICS	Nominal value	Unit
Flame retardant level
0.80 mm	V-0
1.60 mm
3.20 mm
Glowing wire flammability index
0.80 mm	960	℃
1.6 mm	960	℃
3.2 mm	960	℃
Igniting temperature of the hot wire
0.8 mm	775	℃
1.6 mm	800	℃
3.2 mm	825	℃
Extreme oxygen index	35	%
French Fire Index	F2
French Smoke Index	I3

Supplementary information	Nominal value	Unit	Test method
European Railway Certification
R22	HL2
R23	HL3

Process Conditions
Injection	Nominal value	Unit	Test method
Injection instructions	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.20	%
Temperature at the rear of the barrel	230 to 235	°C
Temperature in the middle of the barrel	235 to 240	°C
Front temperature of material barrel	240 to 245	°C
Mold temperature	60 to 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.