| TECHNYLSTAR® SX 218L1 V50 BLACK 38N-K is based on a patented high flow polyamide 6 resin (Technylstar), reinforced with 50% glass fibre, heat & improved UV stabilized, for injection moulding. Due to its outstanding flow caracteristics, this grade allows more freedom in mold and part design versus a standard polyamide solution.&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Heat Stabilized,Weather resistance is good,High liquidity |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.56 | g/cm³ | |
| Water absorption rate | |||
| 23℃，24hr | 0.70 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 17500 | MPa | |
| tensile strength | |||
| fracture | 210 | MPa | |
| Fracture, 23 ℃ | 220 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.8 | % | |
| Fracture, 23 ℃ | 2.4 | % | |
| Bending modulus | |||
| 23℃ | 15000 | MPa | |
| bending strength | 300 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 13 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 209 | ℃ | |
| 1.8 MPa, unannealed | 210 | ℃ | |
| Melting temperature | 220 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Recommended maximum moisture content | 0.20 | % | |
| Temperature at the rear of the barrel | 230 to 235 | °C | |
| Temperature in the middle of the barrel | 235 to 245 | °C | |
| Front temperature of material barrel | 245 to 250 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |