| About |
|---|
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Resistance, Good,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water absorption rate | 0.8 | % | ISO 62 |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Extreme oxygen index | 23 | % | ISO 4589 |
| Flame retardant level | HB | UL 94 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Breaking strength/maximum load | 190/135 | Mpa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3/4 | % | ISO 527-2 |
| Tensile modulus | 10000/7500 | Mpa | ISO 527-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| tracking resistance | 350 | V | IEC 112 |
| Volumetric resistance | 10^15/10^13 | Ω.cm | IEC 93 |
| Relative permittivity | 3.4/4 | IEC 250 | |
| Dielectric loss factor | 0.01/0.11 | kv/mm | IEC 250 |
| Dielectric strength | 34/29 | kv/mm | IEC 243 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | 2.5 | 10^-5·k^-1 | ASTM E-831 |
| melting point | 260 | ℃ | ISO 3146-C |
| Hot deformation temperature | 255 | ℃ | ISO 75-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 80/95 | kJ/m² | ISO 179/1eU | |
| 12/16 | kJ/m² | ISO 179/1eA | |
| Impact strength of cantilever beam notch | 11/16 | kJ/m² | ISO 180/1A（93） |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |