| About |
|---|
| ABS/PA alloy 20% glass fibres reinforced combining excellent dimensional stability, good impact strength, rigidity and chemical resistance with high heat resistance and low shrinkage.&& |
| Product Description | |
|---|---|
| Generic | ABS+PA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good Dimensional Stability,Low contractility,High Heat Resistance,Solvent resistance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，10.0kg | 30 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD：23℃，3.2 mm | 0.70 | % | Internal Method |
| MD：23℃，3.2 mm | 0.40 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.1 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 85.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2/50 |
| Bending modulus | 4600 | MPa | ISO 178 |
| bending strength | 120 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 12.0 | kJ/m² | ASTM D256 |
| -20℃ | 60 | J/m | ASTM D256 |
| 23℃ | 120 | J/m | ASTM D256 |
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 180 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 110 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 185 | ℃ | ISO 306/A50 |
| B50 | 175 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 4.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | > 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Burning rate | |||
| 1.6 mm | < 100 | mm/min | ISO 3795 |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ash Content | |||
| 750℃ | 20 | % | ISO 3451 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 1.0 | hr | |
| Processing (melt) temperature | 240 to 280 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. TARO 002 |
| 3. 0.039 in/min |
| 4. 120°C/hr |
| 5. US FMVSS302 |
| 6. 1 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |