| About |
|---|
| PA6.6, 30% glass fiber reinforced, hydrolysis stabilized, natural&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,HB |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD | 1.1 | % | Internal Method |
| MD | 0.30 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.9 | % | ISO 62 |
| water content | < 0.20 | % | ISO 960 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 10000 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 185 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 11 | kJ/m² | ISO 180-1A |
| 23℃ | 13 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 70 | kJ/m² | ISO 180/1U |
| 23℃ | 80 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 255 | ℃ | ISO 306/B |
| Melting temperature | 262 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | |||
| Solution A | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 70 to 110 | °C | |
| Injection speed | Fast | ||
| Hold pressure | 50.0 to 100 | MPa | |
| Back pressure | Low | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10 K/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |