| PET, 30% glass fiber reinforced, flame retardant – halogen & red phosphorus free, heat stabilized, natural&& |
| Product Description | |
|---|---|
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Low to no phosphorus content,Heat Stabilized |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.2 | % | ISO 294-4 |
| TD | 0.9 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，50% RH | 0.200 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 100 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.5 | % | ISO 527-2 |
| Tensile modulus | 12000 | MPa | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 250 | ℃ | ISO 11357 |
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 220 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+16 | Ω.cm | IEC 60093 |
| Surface resistance | 1.0E+14 | Ω.cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Igniting temperature of the hot wire | |||
| 2 mm | 775 | ℃ | IEC 60695-2-12 |
| Relative temperature of heating wire | |||
| 2.00mm | 960 | ℃ | IEC 60695-2-13 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Maintain pressure | 60.0 -100.0 | MPa | |
| Injection speed | 中等-快 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.00 | kJ/m² | ISO 180-1A |
| -30℃ | 6.00 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 -140 | °C | |
| Drying time | 4.00 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 260-280 | °C | |
| Central temperature of the barrel | 260-280 | °C | |
| Barrel front temperature | 260-280 | °C | |
| Die temperature | 260-280 | °C | |
| Mold temperature | 120-140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10 K/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |