| Product Description | |
|---|---|
| Supplier | Chemours |
| Material Status | Commercial: Negative |
| Features | Weather resistance is good,Good Electrical Properties,High purity,Heat Stabilized,Low coefficient of friction,Solvent resistance,High liquidity,Good flexibility,Heat Resistance, Good,Low smoke,V-0,Low moisture absorption,Good melt strength,Food contact compliance |
| Availabilitys | Europe,North America,Latin America,Asia Pacific |
| Process Methods | Extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.15 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 372℃，5.0kg | 16 | g/10min | ASTM D3307 |
| 372℃，5.0kg | 16 | g/10min | ISO 12086 |
| Water absorption rate | |||
| 24hr | < 0.030 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 55 | ISO 868 | |
| Shaw’s D | 55 | ASTM D2240 | |
| tensile strength | ASTM D3307 | ||
| 23℃ | 25.0 | MPa | ASTM D3307 |
| 250℃ | 14.0 | MPa | ASTM D3307 |
| tensile strength | ISO 12086 | ||
| 23℃ | 25.0 | MPa | ISO 12086 |
| 250℃ | 14.0 | MPa | ISO 12086 |
| Tensile strain | ASTM D3307 | ||
| Fracture, 23 ℃ | 300 | % | ASTM D3307 |
| Fracture, 250 ℃ | 480 | % | ASTM D3307 |
| Tensile strain | ISO 12086 | ||
| Fracture, 23 ℃ | 300 | % | ISO 12086 |
| Fracture, 250 ℃ | 480 | % | ISO 12086 |
| Bending modulus | ASTM D790 | ||
| 23℃ | 590 | MPa | ASTM D790 |
| 250℃ | 55.0 | MPa | ASTM D790 |
| Bending modulus | ISO 178 | ||
| 23℃ | 590 | MPa | ISO 178 |
| 250℃ | 55.0 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 305 | ℃ | ASTM D4591 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+18 | ohms·cm | ISO 1325 |
| Dielectric strength | |||
| 0.25 mm | 80 | kV/mm | ASTM D149 |
| 0.25 mm | 80 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 2.03 | IEC 60250 | |
| 1 MHz | 2.03 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | < 2.0E-4 | IEC 60250 | |
| 1 MHz | < 2.0E-4 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | > 95 | % | ASTM D2863 |
| Extreme oxygen index | > 95 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Critical Shear Rate（372℃） | 56.0 | sec^-1 | |
| MIT flexural strength (200.0 µ m) | 1.5E+4 | Cycles | ASTM D2176 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |