| About |
|---|
| Product Description | |
|---|---|
| Supplier | Chemours |
| Material Status | Commercial: Negative |
| Features | Food contact compliance,Good melt strength,High purity,Low smoke,Good flexibility,Heat Stabilized,Solvent resistance,Weather resistance is good,Good Electrical Properties,Low moisture absorption,Low liquidity,V-0,High ESCR,Low coefficient of friction,Heat Resistance, Good |
| Availabilitys | Europe,Latin America,North America,Asia Pacific |
| Process Methods | Extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.14 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 372℃，5.0kg | 2.0 | g/10min | ISO 12086 |
| 372℃，5.0kg | 2.0 | g/10min | ASTM D3307 |
| Water absorption rate | |||
| 24hr | < 0.030 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 55 | ASTM D2240 | |
| Shaw’s D | 55 | ISO 868 | |
| tensile strength | ASTM D3307 | ||
| 23℃ | 28.0 | MPa | ASTM D3307 |
| 250℃ | 14.0 | MPa | ASTM D3307 |
| tensile strength | ISO 12086 | ||
| 23℃ | 28.0 | MPa | ISO 12086 |
| 250℃ | 14.0 | MPa | ISO 12086 |
| Tensile strain | ASTM D3307 | ||
| Fracture, 23 ℃ | 300 | % | ASTM D3307 |
| Fracture, 250 ℃ | 500 | % | ASTM D3307 |
| Tensile strain | ISO 12086 | ||
| Fracture, 23 ℃ | 300 | % | ISO 12086 |
| Fracture, 250 ℃ | 500 | % | ISO 12086 |
| Bending modulus | ASTM D790 | ||
| 23℃ | 625 | MPa | ASTM D790 |
| 250℃ | 69.0 | MPa | ASTM D790 |
| Bending modulus | ISO 178 | ||
| 23℃ | 625 | MPa | ISO 178 |
| 250℃ | 69.0 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 305 | ℃ | ASTM D4591 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+18 | ohms·cm | ISO 1325 |
| Dielectric strength | |||
| 0.25 mm | 80 | kV/mm | IEC 60243-1 |
| 0.25 mm | 80 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 2.03 | ASTM D150 | |
| 1 MHz | 2.03 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | < 2.0E-4 | ASTM D150 | |
| 1 MHz | < 2.0E-4 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | > 95 | % | ASTM D2863 |
| Extreme oxygen index | > 95 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Critical Shear Rate（372℃） | 12.0 | sec^-1 | |
| MIT flexural strength (200.0 µ m) | 5.0E+5 | Cycles | ASTM D2176 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |