| Features JN1 is unreinforced PA/PPE alloy. JN1 has good properties with excellent heat resistance, excellent dimensional stability, good impact resistence, good chemical resistance Application Junction box Drying Product is dried and packed with a moisture content of <0.16%. Should the Packaging become damaged or be left open too long, then the material must be Dried. A too high moisture content can lead to a reduction of optical and Mechanical properties.&& |
| Product Description | |
|---|---|
| Supplier | Mando |
| Generic | PA+PPO(PPE) |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,High liquidity,Heat Stabilized,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.3 to 1.7 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.40 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 58.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 | % | ASTM D638 |
| Bending modulus | 2260 | MPa | ASTM D790 |
| bending strength | 95.1 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 180 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 185 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 145 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 to 105 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 255 to 295 | °C | |
| Barrel middle temperature | 260 to 295 | °C | |
| Barrel front temperature | 265 to 295 | °C | |
| Nozzle temperature | 270 to 295 | °C | |
| Processing (melt) temperature | 270 to 295 | °C | |
| Mold temperature | 65 to 95 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.12 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |