| About |
|---|
| Telcar TL-2895E X is a general purpose thermoplastic elastomer designed for electrical applications requiring flexibility over a wide temperature range. Telcar TL-2895E X is a medium hardness, low density, sunlight resistant grade that is RoHS compliant. This grade is suitable for both injection molding and extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low liquidity,High elastic,Ultraviolet absorption,Halogen free,Ablation resistance,Good Tensile Strength,Low density |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.878 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 5.5 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 4.08 | MPa | ASTM D412 |
| MD, 100% strain | 5.81 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| TD, 300% strain | 5.19 | MPa | ASTM D412 |
| MD, 300% strain | 7.19 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| fracture | 18.1 | MPa | ASTM D412 |
| MD, fracture | 10.1 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| fracture | 810 | % | ASTM D412 |
| Flow rate, fracture | 580 | % | ASTM D412 |
| tear strength | ASTM D624 | ||
| TD | 58.7 | kN/m | ASTM D624 |
| MD | 55.5 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 23 | % | ASTM D395B |
| 70℃，22 hr | 79 | % | ASTM D395B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 1 second | 85 | ASTM D2240 | |
| Shore A, 5 seconds | 80 | ASTM D2240 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel rear temperature | 199 to 216 | °C | |
| Barrel middle temperature | 213 to 221 | °C | |
| Barrel front temperature | 221 to 227 | °C | |
| Nozzle temperature | 221 to 229 | °C | |
| Processing (melt) temperature | 221 to 229 | °C | |
| Mold temperature | 25 to 66 | °C | |
| Injection pressure | 1.38 to 6.89 | MPa | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 0.172 to 0.345 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Barrel 1 zone temperature | 193 to 210 | °C | |
| Barrel 2 zone temperature | 199 to 216 | °C | |
| Barrel 3 zone temperature | 213 to 221 | °C | |
| Barrel 5 zone temperature | 221 to 227 | °C | |
| Nozzle temperature | 221 to 229 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C, 20 in/min |
| 3. Type 1 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |