Teldene® H03BPMP

About
Typical Applications BOPP films produced at very high speed with excellent processability Used for metallizable film, both as monolayer and in co-extruded structure Engaged for the production of solid phase thermoforming Suitable for raffia application Key Characteristics Easy processing, good optical characteristics Does not contain any slip or anti-blocking agents Calcium stearate free Very good film profile High speed film production High transparency and gloss with high stiffness and strength Food contact approval for specific applications (refer to NATPET)&&

About

Typical Applications BOPP films produced at very high speed with excellent processability Used for metallizable film, both as monolayer and in co-extruded structure Engaged for the production of solid phase thermoforming Suitable for raffia application Key Characteristics Easy processing, good optical characteristics Does not contain any slip or anti-blocking agents Calcium stearate free Very good film profile High speed film production High transparency and gloss with high stiffness and strength Food contact approval for specific applications (refer to NATPET)&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,Good Clarity,Good surface appearance,Optical performance,Food contact compliance,Electroplating,Homopolymer
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	3.0	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1500	MPa	ISO 527-1-2
tensile strength			ISO 527-2/50
yield	33.0	MPa	ISO 527-2/50
fracture	23.0	MPa	ISO 527-2/50
Tensile strain			ISO 527-2/50
yield	12	%	ISO 527-2/50
fracture	> 50	%	ISO 527-2/50
Bending modulus	1400	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	6.2	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	94.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	155	℃	ISO 306/A50

optical performance	Nominal value	Unit	Test method
Haze
20 µm	0.80	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	240 to 260	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.