| An amorphous thermoplastic polyetherimide, stock shapes from ULTEM® resin possess a combination of useful characteristics, including high strength at elevated temperatures, high modulus, and broad chemical resistance. Tempalux stock shapes are inherently flame resistant with low smoke emission. Tempalux stock shapes display property retention and resistance to environmental stress cracking when exposed to a wide variety of chemicals. The standard color of Tempalux stock shapes is light amber. Glass filled grades appear tan or greenish in color. Tempalux rod, slab, and tubular bar are air annealed for stress relief. Applications Include: Burn-in test sockets Connectors Automotive components Valves, electrical fittings Advantages of Tempalux: Inherent flame resistance Extremely low NBS smoke evolution Superior limiting oxygen index Exceptional tensile and flexural strength Broad chemical resistance UV stable FDA compliant&& |
| Product Description | |
|---|---|
| Supplier | Westlake Plastics |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Low smoke,Flame Characteristics,Food contact compliance,Good Tensile Strength,Solvent resistance,High ESCR,Amorphous,5VA |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 0.25 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 1300 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 210 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 200 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 5.6E-5 | 1/℃ | ASTM D696 |
| Thermal conductivity coefficient | 0.22 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | 33 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 3.15 | ASTM D150 | |
| Dissipation factor | |||
| 1 kHz | 1.3E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.90 mm | 5VA | UL 94 | |
| Extreme oxygen index | 47 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 109 | ASTM D785 | |
| Tensile modulus | 2960 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 105 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 7.0 | % | ASTM D638 |
| fracture | 60 | % | ASTM D638 |
| Bending modulus | 3310 | MPa | ASTM D790 |
| bending strength | |||
| yield | 152 | MPa | ASTM D790 |
| Compression modulus | 3310 | MPa | ASTM D695 |
| compressive strength | 151 | MPa | ASTM D695 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |