| About |
|---|
| Tenac™ 9054 is an Acetal (POM) Homopolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ 9054 include engineering/industrial parts and housings. Characteristics include: Flame Rated Antistatic Fast Molding Cycle High Flow Homopolymer&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | Paraformaldehyde |
| Material Status | Commercial: Active |
| Features | Low warping,High liquidity,Low Viscosity,Quick molding cycle,Antistatic property,Homopolymer,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 70 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 1.7 to 2.1 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr，50% RH | 0.20 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | 37 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 172 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 165 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 136 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 105 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 1.0E-4 | 1/℃ | ASTM D696，ISO 11359-2 |
| specific heat | 1470 | J/kg/℃ | |
| Thermal conductivity coefficient | 0.23 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 to 1.0E+17 | ohms | ASTM D257 |
| Volume resistivity | |||
| 23℃ | 1.0E+15 to 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1 MHz | 3.80 | ASTM D150 | |
| Dissipation factor | |||
| 23℃，1 MHz | 7.0E-3 | ASTM D150 | |
| Arc resistance | 250 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 94 | ASTM D785 | |
| R-level | 120 | ASTM D785 | |
| Tensile modulus | 3500 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 74.0 | MPa | ISO 527-2 |
| — | 73.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 12 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 3300 | MPa | ASTM D790 , ISO 178 |
| bending strength | 112 | MPa | ASTM D790 |
| Taber abraser | 13.0 | mg | ASTM D1044 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |