Tenite™ Butyrate 572A1V95316 Smoke, Trsp

About
Tenite™ cellulosic plastics are noted for their excellent balance of properties – toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 572-16 contains an odor mask lubricant and an ultra-violet inhibitor (UVI). It has a plasticizer level of 16%.&&

About

Tenite™ cellulosic plastics are noted for their excellent balance of properties – toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 572-16 contains an odor mask lubricant and an ultra-violet inhibitor (UVI). It has a plasticizer level of 16%.&&

Product Description
Supplier	Eastman
Generic	CAB
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Good Clarity,Good flexibility,Good surface appearance,High impact resistance,Good Dimensional Stability,Renewable resources,Good Hardness,High Heat Resistance,Plasticizing
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.19	g/cm³	ASTM D792
Water absorption rate
23℃，24hr	1.2	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ASTM D256
-40℃	100	J/m	ASTM D256
23℃	530	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, annealed	67.0	℃	ASTM D648
0.45 MPa, annealed	79.0	℃	ASTM D648

Supplementary information	Nominal value	Unit	Test method
Heating reduction
72 hr，80℃	0.90	%	ASTM D707

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, 23 ℃	31.0	MPa	ASTM D638
Yield, 23 ℃	30.3	MPa	ASTM D638
Tensile strain
Fracture, 23 ℃	26	%	ASTM D638
Bending modulus
23℃	1160	MPa	ASTM D790
Rockwell hardness
R-level	60		ASTM D785

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.