| About |
|---|
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | PEN |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 18 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-1-2 |
| Tensile Strength | |||
| yield | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield yld | 7.0 | % | ISO 527-2/50 |
| Broken BRK | 15 | % | ISO 527-2/50 |
| Flexural Modulus | 2250 | MPa | ISO 178 |
| Flexural Strength | 99.0 | MPa | ISO 178 |
| Rockwell hardness | 107 | M | ASTM D-785 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 98 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 91 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 105 | ℃ | ISO 75-2/B |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Molding Temperature | 280-310 | ℃ | |
| Mold Temperature | 60-90 | ℃ | |
| Injection pressure | 60-140 | MPa | |
| Drying Temperature | 140-160 | ℃ | |
| Drying Time | 5-8 | hr | |
| Hopper Temperature | 100-120 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |