| About |
|---|
| Terblend® N 3158 is an 9% mineral-filled ABS/PA blend with good dimensional stability, enhanced rigidity and excellent heat resistance, so that this grade can be applied for online-painting. FEATURES High dimensional stability High rigidity Excellent heat resistance for online-painting Mineral filled (9%) APPLICATIONS Automotive exterior parts Fenders&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS+PA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,High Heat Resistance |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，10 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 1.1 to 1.4 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.3 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2900 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 50.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| MD, fracture | > 10 | % | ISO 527-3 |
| Yield, 23 ℃ | 3.0 | % | ISO 527-2 |
| Fracture, 23 ℃ | > 10 | % | ISO 527-2 |
| Bending modulus | 3000 | MPa | ISO 178 |
| bending strength | 88.0 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 160 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 8.0 | kJ/m² | ISO 180-A |
| 23℃ | 10 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 132 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 92.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 245 | ℃ | ASTM D1525 3 |
| B50 | 160 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 7.5E-3 | IEC 60250 | |
| 1 MHz | 0.015 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 80 | °C | |
| Injection Velocity | 40 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |