| About |
|---|
| Terblend® N NG-02 EF is an 8% glass fiber reinforced UV-stabilized ABS/PA blend with enhanced dimensional stability, rigidity and high flowability. FEATURES High dimensional stability Excellent flow for high surface quality appearance Enhanced softening temperature Enhanced rigidity UV-stabilized APPLICATIONS Automotive parts Motorcycle fairings Truck cabin parts&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS+PA |
| Material Status | Commercial: Active |
| Features | High liquidity,Weather resistance is good,Good surface appearance,Good Dimensional Stability |
| Availabilitys | Latin America,North America,Asia Pacific,Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 240℃，10 kg | 40.0 | cm³/10min | ISO 1133 |
| Molding shrinkage | 0.60 | % | ISO 294-4 |
| Water Absorption | |||
| Balanced Equilibrium, 23 ℃, 50% RH | 1.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield yld, 23 ℃ | 55.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Strength | 85.0 | MPa | ISO 178 |
| Ball indentation hardness | 99 | MPa | ISO 2039-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strain | |||
| Yield yld, 23 ℃ | 3.0 | % | ISO 527-2 |
| MD, broken brk | 6.0 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 11 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 35 | kJ/m² | |
| 23℃ | 50 | kJ/m² | |
| Izod Notched Impact strength | ISO 180/A | ||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 12 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 130 | ℃ | ISO 75-2/B | |
| 80.0 | ℃ | ISO 75-2/A | |
| Vicat Softening Temperature | |||
| A50 | 200 | ℃ | ISO 306/A50 |
| B50 | 118 | ℃ | ISO 306 |
| Coeff. of linear thermal expansion | |||
| MD | 6.0E-5 | 1/℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistance | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.018 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Melt Temperature | 240-270 | °C | |
| Mold Temperature | 60-80 | °C | |
| Drying Temperature | 80-90 | ℃ | |
| Drying Time | 4-8 | hr | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |