| About |
|---|
| Terblend® S is a UV-stabilized ASA/PA blend with high impact strength, easy flow and pronounced color fastness. It is especially suitable for unpainted highly UV-exposed automotive interior parts. FEATURES Enhanced UV resistance and color fastness Excellent flow for high surface quality appearance High impact strength UV-stabilized APPLICATIONS Unpainted automotive interior parts Trim for convertibles Under the windscreen interior applications&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ASA+PA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,High impact resistance,Good liquidity |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 240℃，10 kg | 60.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.80 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.5 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2100 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 50.0 | MPa | ISO 527-2 |
| Bending modulus | 2000 | MPa | ISO 178 |
| bending strength | 65.0 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strain | |||
| Yield, 23 ℃ | 3.3 | % | ISO 527-2 |
| MD, fracture | 25 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 9.0 | kJ/m² | |
| 23℃ | 70 | kJ/m² | |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 8.0 | kJ/m² | |
| 23℃ | 65 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 92.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 65.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 205 | ℃ | ISO 306/A50 |
| B50 | 110 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 1.0E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.018 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 40.0 to 80.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |