| Partially aromatic PA66 blend with 50% glass fiber proportions and heat stabilized. The product tends to reduced warpage and has improved flow characteristics. For injection-moulded components with high requirements to isotropic strength properties.&& |
| Product Description | |
|---|---|
| Supplier | TER |
| Generic | PA 66+PA 6I/6T |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Good liquidity,Aromatic,Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm³ | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 4.0 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.4 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 17500 | MPa | |
| tensile strength | |||
| fracture | 220 | MPa | |
| Tensile strain | |||
| fracture | 2.5 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 90 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 255 | ℃ | |
| 1.8 MPa, unannealed | 244 | ℃ | |
| Vicat Softening Temp | 210 | ℃ | |
| Melting temperature | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | |
| Dielectric strength | 33 | kV/mm | |
| Compared to the leakage tracing index | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |