| About |
|---|
| PA66 with partially aromatic content, 50 % glass fibre reinforcement as well as heat and hydrolysis stabilisation. For injection moulding parts with high stiffness, good heat resistance and low water absorption.&& |
| Product Description | |
|---|---|
| Supplier | TER |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low or no water absorption,Aromatic,High Heat Resistance,Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 17000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 235 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 1.5 | % | |
| fracture | 2.5 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 88 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 265 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 245 | ℃ | ISO 75-2/A |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |