| About |
|---|
| Terluran® GP-25 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector. FEATURES Excellent colorability Medium flow Good impact resistance Good heat distortion resistance High quality surface finish and gloss APPLICATIONS Injection molding Appliance housings Household and sanitary appliances Toys Automotive components&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Moderate liquidity,Good coloring |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：2.0 mm | 0.7 | % | ISO 294-4 |
| MD：2.0 mm | 0.4 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，50% RH | 0.95 | % | ISO 62 |
| 23℃，24hr | 0.21 | % | ISO 62 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 25 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 44 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 2.4 | % | ISO 527-2 |
| Fracture, 23 ℃ | 12 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 2300 | MPa | ISO 527-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | 15 | YI | DIN6167 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 93 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 97 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| A50 | 103 | ℃ | ISO 306 |
| B50 | 95 | ℃ | ISO 306/A50 |
| Melting temperature | 220-260 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5-1.1E-4 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.170 | W/m/K | DIN 52612 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | >=1.0E+15 | Ω.cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| All color | 1.50mm | HB | UL-94 |
| All color | 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 125 | kJ/m² | ISO 179/1eU |
| -30℃ | 90 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 19 | kJ/m² | ISO 179/1eA |
| -30℃ | 7 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 22 | kJ/m² | ISO 180-1A |
| -30℃ | 7 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60-80 | °C | |
| Drying time | 2.0-3.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 180-220 | °C | |
| Barrel middle temperature | 190-230 | °C | |
| Barrel front temperature | 210-240 | °C | |
| Nozzle temperature | 200-240 | °C | |
| Mold temperature | 40-80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |