| About |
|---|
| Terluran® GP-35 is high-flow, general purpose injection molding grade with good ductility, intended for moldings with thin walls and/or adverse flow length to wall ratio. FEATURES Excellent colorability High flowability Good impact resistance Good heat distortion resistance High quality surface finish and gloss APPLICATIONS Injection molding Thin wall components for telecommunications Household and sanitary appliances Toys Automotive components&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,High liquidity,Ductility,Good coloring |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：2.0 mm | 0.55 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.95 | % | ISO 62 |
| 23℃，50% RH | 0.24 | % | ISO 62 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | 15 | YI | DIN6167 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 95 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 92 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 102 | ℃ | ISO 306/A50 |
| B50 | 95 | ℃ | ISO 306 |
| Thermal conductivity coefficient | 0.17 | W/m/K | DIN 52612 |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+15 | Ω.cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80mm | HB | UL-94 | |
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 130 | kJ/m² | ISO 179/1eU |
| -30℃ | 90 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 19 | kJ/m² | ISO 179/1eA |
| -30℃ | 7 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 22 | kJ/m² | ISO 180-1A |
| -30℃ | 7 | kJ/m² | ISO 180-1A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 99 | MPa | ISO 2039-1 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.4 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 2300 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 65 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2－4 | Hr | |
| Injection temperature | |||
| Mold temperature | 30-60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |