| About |
|---|
| Terluran® HI-10 is an medium flow, injection molding grade with very high resistance to impact with excellent heat distortion and suitable for injection molding and extrusion. FEATURES High toughness Very high impact Medium flow Great mechanical strength and rigidity High impact at sub-zero temperatures APPLICATIONS Injection molding Compounding Appliance housings Lawn & garden components requiring superior toughness&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High impact resistance,Moderate liquidity,low-temperature impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：2.0 mm | 0.55 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，50% RH | 0.21 | % | ISO 62 |
| 23℃，24hr | 1.00 | % | ISO 62 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | 15 | YI | DIN6167 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 93 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 97 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 90 | ℃ | ISO 306 |
| A50 | 103 | ℃ | ISO 306/A50 |
| Linear coefficient of thermal expansion | |||
| TD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.17 | W/m/K | DIN 52612 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+16 | Ω.cm | IEC 60093 |
| Insulation strength | 25 | KV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 23℃ | 2.9 | 100 Hz | IEC 60250 |
| 23℃ | 2.8 | 1 MHz | IEC 60250 |
| Dissipation factor | |||
| 23℃ | 8.2E-3 | 1 MHz | IEC 60250 |
| 23℃ | 5.4E-3 | 100 Hz | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| All color | 0.80mm | HB | UL-94 |
| All color | 3.00mm | HB | UL-94 |
| All color | 1.50mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | N/D | kJ/m² | ISO 179/1eU |
| -30℃ | 140 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eA |
| -30℃ | 13 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 36 | kJ/m² | ISO 180-1A |
| -30℃ | 14 | kJ/m² | ISO 180-1A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 74 | MPa | ISO 2039-1 |
| tensile strength | |||
| 23℃ | 38 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.8 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 1900 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 56 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion molding conditions | Nominal value | Unit | Test method |
| Drying temperature | 60-80 | °C | |
| Drying time | 2.0-3.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 180-220 | °C | |
| Barrel middle temperature | 190-230 | °C | |
| Barrel front temperature | 210-240 | °C | |
| Nozzle temperature | 200-240 | °C | |
| Mold temperature | 40-80 | °C | |
| Drying temperature | 60-80 | °C | |
| Drying time | 2.0-3.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| First zone temperature | 150-200 | °C | |
| Zone 2 temperature | 160-210 | °C | |
| Third zone temperature | 170-220 | °C | |
| Fourth zone temperature | 180-230 | °C | |
| Fifth zone temperature | 190-240 | °C | |
| Die temperature | 210-250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |