| About |
|---|
| Terluran® SP-6 is a high impact extrusion grade. FEATURES High impact strength Suitable for co-extrusion APPLICATIONS Extrusion Sheets and profiles Household and sanitary appliances&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 5.50 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 1.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.21 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 13 | kJ/m² | ISO 179 |
| 23℃ | 35 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 140 | kJ/m² | ISO 179 |
| 23℃ | 无断裂 | ISO 179 | |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 14 | kJ/m² | ISO 180-A |
| 23℃ | 36 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 97.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 93.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 103 | ℃ | ISO 306/A50 |
| B50 | 90.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 to 1.1E-4 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.17 | W/m/K | DIN 52612 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 5.4E-3 | IEC 60250 | |
| 1 MHz | 8.2E-3 | IEC 60250 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | 15 | YI | DIN 6167 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 74.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1900 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 38.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 2.8 | % | ISO 527-2 |
| Nominal tensile fracture strain | |||
| 23℃ | 9.0 | % | ISO 527-2 |
| bending strength | 56.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Melt temperature | 210 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |