| About |
|---|
| Terlux® 2802 is a standard injection molding grade based on a MABS polymer. Terlux® 2802 offers an unique combination of properties, such as a balanced stiffness/toughness ratio and the high transparency well known in SAN molding compositions. FEATURES Excellent transparency Good resistance to chemicals Good stiffness and surface finish High impact strength APPLICATIONS Cosmetic packaging Homeware Housings Toys, sport and leisure&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS transparent |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good surface appearance,High impact resistance,Solvent resistance,Rigid-tough balance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Apparent density | 0.59 | g/cm³ | |
| Melt Volume Rate | ISO 1133 | ||
| 220℃，10 kg | 2.00 | cm³/10min | ISO 1133 |
| 220℃，21.6 kg | 17.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.70 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 2.0 | kJ/m² | ISO 179 |
| 23℃ | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 80 | kJ/m² | ISO 179 |
| 23℃ | 120 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 90.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 94.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 105 | ℃ | ISO 306/A50 |
| B50 | 93.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 to 1.1E-4 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.17 | W/m/K | DIN 52612 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 100 Hz | 2.90 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 0.016 | IEC 60250 | |
| 1 MHz | 0.014 | IEC 60250 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.540 | ISO 489 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 48.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 4.0 | % | ISO 527-2 |
| Nominal tensile fracture strain | |||
| 23℃ | 12 | % | ISO 527-2 |
| Tensile creep modulus | |||
| 1000 hr | 1250 | MPa | ISO 899-1 |
| bending strength | 70.0 | MPa | ISO 178 |
| Ball hardness | 70.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 50 to 75 | °C | |
| Injection Velocity | 200 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. With external lubricant |
| 3. 4h/80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |