| Linear low density polyethylene, butene copolymer, blended with high-density polyethylene, contains processing additives. Suitable for blown film applications.&& |
| Product Description | |
|---|---|
| Generic | HDPE+LLDPE |
| Material Status | Commercial: Active |
| Features | Renewable resources,Copolymer,Butylene copolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.70 to 0.85 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 0.900 to 1.10 | cm³/10min | ISO 1133 |
| Biomass content | |||
| Carbon | 90 | % | ASTM D6866 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 330 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 23 | % | ISO 527-2 |
| fracture | > 300 | % | ISO 527-2 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD，20 µm | 290 | MPa | ISO 527-3 |
| TD，20 µm | 310 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| yield | 11.0 | MPa | ISO 527-2 |
| MD, yield, 20 µ m | 37.0 | MPa | ISO 527-3 |
| TD, yield, 20 µ m | 32.0 | MPa | ISO 527-3 |
| MD, fracture, 20 µ m | 36.0 | MPa | ISO 527-3 |
| TD, fracture, 20 µ m | 31.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, yield, 20 µ m | 680 | % | ISO 527-3 |
| TD, yield, 20 µ m | 690 | % | ISO 527-3 |
| MD, fracture, 20 µ m | 680 | % | ISO 527-3 |
| TD, fracture, 20 µ m | 690 | % | ISO 527-3 |
| tear strength | ISO 6383-2 | ||
| MD，20 µm | 50.0 | kN/m | ISO 6383-2 |
| TD，20 µm | 150.0 | kN/m | ISO 6383-2 |
| Spencer Impact | |||
| 20.0 µm | 130.0 | kN/m | ASTM D3420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 130 to 145 | ℃ | ISO 3146 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. BUR 2.4 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |