Texin® 270 - SOLIAO

About
Texin 270 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 70D. It can be processed by injection molding; extrusion processes are not recommended.&&

Product Description
Supplier	Covestro
Generic	TPU-酯
Material Status	Commercial: Active
Features	Good Rigidity,Good tear strength,Grease resistance,Fuel resistance
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.24	g/cm³	ASTM D792
Density	1.24	g/cm³	ISO 1183
Shrinkage rate			ISO 2577
TD：2.54 mm	0.80	%	ASTM D955
MD：2.54 mm	0.80	%	ASTM D955
TD：2.54 mm	0.80	%	ISO 2577
MD：2.54 mm	0.80	%	ISO 2577

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	70		ISO 868
Shaw’s D	70		ASTM D2240
Bending modulus			ASTM D790
-30℃	2910	MPa	ASTM D790
23℃	724	MPa	ASTM D790
70℃	103	MPa	ASTM D790
Bending modulus			ISO 178
-30℃	2910	MPa	ISO 178
23℃	724	MPa	ISO 178
70℃	103	MPa	ISO 178
Taber abraser
1000 cycles, 1000 g, H-18 wheels	90.0	mg	ISO 4649
1000 cycles, 1000 g, H-18 wheels	90.0	mg	ASTM D1044

elastic body	Nominal value	Unit	Test method
tensile strength
yield	56.6	MPa	ISO 37
yield	56.6	MPa	ASTM D412
300% strain	42.8	MPa	ASTM D412
300% strain	42.8	MPa	ISO 37
100% strain	29.0	MPa	ISO 37
100% strain	29.0	MPa	ASTM D412
50% strain	28.3	MPa	ISO 37
50% strain	28.3	MPa	ASTM D412
Tensile strain
fracture	400	%	ASTM D412
fracture	400	%	ISO 37
tear strength	228	kN/m	ASTM D624
tear strength	230	kN/m	ISO 34-1
Compression deformation			ASTM D395B
23℃，22 hr	30	%	ASTM D395B
23℃，22 hr	50	%	ASTM D395B
70℃，22 hr	45	%	ASTM D395B
70℃，22 hr	85	%	ASTM D395B
Compression deformation			ISO 815
23℃，22 hr	50	%	ISO 815
23℃，22 hr	30	%	ISO 815
70℃，22 hr	85	%	ISO 815
70℃，22 hr	45	%	ISO 815
Basho’s elasticity	55	%	ASTM D2632

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	38.0	℃	ISO 75-2/A
1.8 MPa, unannealed	38.0	℃	ASTM D648
0.45 MPa, unannealed	46.0	℃	ASTM D648
0.45 MPa, unannealed	46.0	℃	ISO 75-2/B
Embrittlement temperature	< -68.0	℃	ASTM D746
Embrittlement temperature	< -68.0	℃	ISO 974
Glass transition temperature	0.00	℃	DMA
Vicat Softening Temp	158	℃	ASTM D1525 4
Vicat Softening Temp	158	℃	ISO 306/50
Linear coefficient of thermal expansion
MD	9.9E-5	1/℃	ASTM D696

Aging performance	Nominal value	Unit	Test method
The rate of change in tensile strength in air			ASTM D573
100℃，70 hr	17	%	ASTM D573
100% Strain，100℃，70 hr	10	%	ASTM D573
300% Strain，100℃，70 hr	12	%	ASTM D573
100℃，168 hr	10	%	ASTM D573
100% Strain，100℃，168 hr	2.0	%	ASTM D573
300% Strain，100℃，168 hr	6.0	%	ASTM D573
100℃，336 hr	9.0	%	ASTM D573
100% Strain，100℃，336 hr	2.0	%	ASTM D573
300% Strain，100℃，336 hr	4.0	%	ASTM D573
100℃，504 hr	21	%	ASTM D573
100% Strain，100℃，504 hr	1.0	%	ASTM D573
300% Strain，100℃，504 hr	2.0	%	ASTM D573
The rate of change in tensile strength in air			ISO 216
100℃，70 hr	17	%	ISO 216
100% Strain 100℃，70 hr	10	%	ISO 216
300% Strain 100℃，70 hr	12	%	ISO 216
100℃，168 hr	10	%	ISO 216
100% Strain 100℃，168 hr	2.0	%	ISO 216
300% Strain 100℃，168 hr	6.0	%	ISO 216
100℃，336 hr	9.0	%	ISO 216
100% Strain 100℃，336 hr	2.0	%	ISO 216
300% Strain 100℃，336 hr	4.0	%	ISO 216
100℃，504 hr	21	%	ISO 216
100% Strain 100℃，504 hr	1.0	%	ISO 216
300% Strain 100℃，504 hr	2.0	%	ISO 216
The rate of change in ultimate elongation in air			ASTM D573
100℃，70 hr	3.0	%	ASTM D573
100℃，168 hr	3.0	%	ASTM D573
100℃，336 hr	3.0	%	ASTM D573
100℃，504 hr	15	%	ASTM D573
Changes in tensile stress during fracture in air			ISO 216
100℃，70 hr	3.0	%	ISO 216
100℃，168 hr	3.0	%	ISO 216
100℃，336 hr	3.0	%	ISO 216
100℃，504 hr	15	%	ISO 216
The rate of change in hardness of a hardness tester in the air			ASTM D573
Shore D, 100 ℃, 70 hr	1.0		ASTM D573
Shore D, 100 ℃, 168 hr	-6.0		ASTM D573
Shore D, 100 ℃, 336 hr	-5.0		ASTM D573
Shore D, 100 ℃, 504 hr	-1.0		ASTM D573
The rate of change of Shore hardness in air			ISO 216
Shore D, 100 ℃, 70 hr	1.0		ISO 216
Shore D, 100 ℃, 168 hr	-6.0		ISO 216
Shore D, 100 ℃, 336 hr	-5.0		ISO 216
Shore D, 100 ℃, 504 hr	-1.0		ISO 216
The rate of change in tensile strength			ASTM D471
23℃，70 hr，in Reference Fuel A（Isooctane）	-4.0	%	ASTM D471
100% Strain，23℃，70 hr，in Reference Fuel A（Isooctane）	-4.0	%	ASTM D471
300% Strain，23℃，70 hr，in Reference Fuel A（Isooctane）	-2.0	%	ASTM D471
23 ℃, 70 hr, methanol	10	%	ASTM D471
100% Strain，23℃，70 hr，in Reference Fuel C	-4.0	%	ASTM D471
300% Strain，23℃，70 hr，in Reference Fuel C	-1.0	%	ASTM D471
23℃，168 hr，in Reference Fuel A（Isooctane）	-5.0	%	ASTM D471
100% Strain，23℃，168 hr，in Reference Fuel A（Isooctane）	-3.0	%	ASTM D471
300% Strain，23℃，168 hr，in Reference Fuel A（Isooctane）	-4.0	%	ASTM D471
23 ℃, 168 hr, methanol	3.0	%	ASTM D471
100% Strain，23℃，168 hr，in Reference Fuel C	-6.0	%	ASTM D471
300% Strain，23℃，168 hr，in Reference Fuel C	10	%	ASTM D471
23℃，336 hr，in Reference Fuel A（Isooctane）	0.0	%	ASTM D471
100% Strain，23℃，336 hr，in Reference Fuel A（Isooctane）	-3.0	%	ASTM D471
300% Strain，23℃，336 hr，in Reference Fuel A（Isooctane）	4.0	%	ASTM D471
23℃，336 hr，in Reference Fuel C	8.0	%	ASTM D471
100% Strain，23℃，336 hr，in Reference Fuel C	-18	%	ASTM D471
300% Strain，23℃，336 hr，in Reference Fuel C	-4.0	%	ASTM D471
23℃，504 hr，in Reference Fuel A（Isooctane）	-2.0	%	ASTM D471
100% Strain，23℃，504 hr，in Reference Fuel A（Isooctane）	-1.0	%	ASTM D471
300% Strain，23℃，504 hr，in Reference Fuel A（Isooctane）	-1.0	%	ASTM D471
23℃，504 hr，in Reference Fuel C	9.0	%	ASTM D471
100% Strain，23℃，504 hr，in Reference Fuel C	-21	%	ASTM D471
300% Strain，23℃，504 hr，in Reference Fuel C	-2.0	%	ASTM D471
100 ℃, 70 hr, in ASTM # 1 oil	20	%	ASTM D471
100% Strain，100℃，70 hr，in ASTM #1 Oil	2.0	%	ASTM D471
300% Strain，100℃，70 hr，in ASTM #1 Oil	8.0	%	ASTM D471
100 ℃, 70 hr, in ASTM # 3 oil	13	%	ASTM D471
100% Strain，100℃，70 hr，in ASTM #3 Oil	0.0	%	ASTM D471
300% Strain，100℃，70 hr，in ASTM #3 Oil	8.0	%	ASTM D471
100℃，168 hr，in ASTM #1 Oil	7.0	%	ASTM D471
100% Strain，100℃，168 hr，in ASTM #1 Oil	-1.0	%	ASTM D471
300% Strain，100℃，168 hr，in ASTM #1 Oil	7.0	%	ASTM D471
100℃，168 hr，in ASTM #3 Oil	29	%	ASTM D471
100% Strain，100℃，168 hr，in ASTM #3 Oil	-1.0	%	ASTM D471
300% Strain，100℃，168 hr，in ASTM #3 Oil	4.0	%	ASTM D471
100℃，336 hr，in ASTM #1 Oil	2.0	%	ASTM D471
100% Strain，100℃，336 hr，in ASTM #1 Oil	-3.0	%	ASTM D471
300% Strain，100℃，336 hr，in ASTM #1 Oil	-3.0	%	ASTM D471
100℃，336 hr，in ASTM #3 Oil	32	%	ASTM D471
100% Strain，100℃，336 hr，in ASTM #3 Oil	-2.0	%	ASTM D471
300% Strain，100℃，336 hr，in ASTM #3 Oil	-2.0	%	ASTM D471
100℃，504 hr，in ASTM #1 Oil	8.0	%	ASTM D471
100% Strain，100℃，504 hr，in ASTM #1 Oil	-6.0	%	ASTM D471
300% Strain，100℃，504 hr，in ASTM #1 Oil	-11	%	ASTM D471
100℃，504 hr，in ASTM #3 Oil	20	%	ASTM D471
100% Strain，100℃，504 hr，in ASTM #3 Oil	-8.0	%	ASTM D471
300% Strain，100℃，504 hr，in ASTM #3 Oil	-11	%	ASTM D471
The rate of change in tensile strength			ISO 175
23℃，70 hr，in Reference Fuel A（Isooctane）	-4.0	%	ISO 175
100% Strain，23℃，70 hr，in Reference Fuel A（Isooctane）	-4.0	%	ISO 175
300% Strain，23℃，70 hr，in Reference Fuel A（Isooctane）	-2.0	%	ISO 175
23 ℃, 70 hr, methanol	10	%	ISO 175
100% Strain，23℃，70 hr，in Reference Fuel C	-4.0	%	ISO 175
300% Strain，23℃，70 hr，in Reference Fuel C	-1.0	%	ISO 175
23℃，168 hr，in Reference Fuel A（Isooctane）	-5.0	%	ISO 175
100% Strain，23℃，168 hr，in Reference Fuel A（Isooctane）	-3.0	%	ISO 175
300% Strain，23℃，168 hr，in Reference Fuel A（Isooctane）	-4.0	%	ISO 175
23 ℃, 168 hr, methanol	3.0	%	ISO 175
100% Strain，23℃，168 hr，in Reference Fuel C	-6.0	%	ISO 175
300% Strain，23℃，168 hr，in Reference Fuel C	10	%	ISO 175
23℃，336 hr，in Reference Fuel A（Isooctane）	0.0	%	ISO 175
100% Strain，23℃，336 hr，in Reference Fuel A（Isooctane）	-3.0	%	ISO 175
300% Strain，23℃，336 hr，in Reference Fuel A（Isooctane）	4.0	%	ISO 175
23℃，336 hr，in Reference Fuel C	8.0	%	ISO 175
100% Strain，23℃，336 hr，in Reference Fuel C	-18	%	ISO 175
300% Strain，23℃，336 hr，in Reference Fuel C	-4.0	%	ISO 175
23℃，504 hr，in Reference Fuel A（Isooctane）	-2.0	%	ISO 175
100% Strain，23℃，504 hr，in Reference Fuel A（Isooctane）	-1.0	%	ISO 175
300% Strain，23℃，504 hr，in Reference Fuel A（Isooctane）	-1.0	%	ISO 175
23℃，504 hr，in Reference Fuel C	9.0	%	ISO 175
100% Strain，23℃，504 hr，in Reference Fuel C	-21	%	ISO 175
300% Strain，23℃，504 hr，in Reference Fuel C	-2.0	%	ISO 175
100 ℃, 70 hr, in ASTM # 1 oil	20	%	ISO 175
100% Strain，100℃，70 hr，in ASTM #1 Oil	2.0	%	ISO 175
300% Strain，100℃，70 hr，in ASTM #1 Oil	8.0	%	ISO 175
100 ℃, 70 hr, in ASTM # 3 oil	13	%	ISO 175
100% Strain，100℃，70 hr，in ASTM #3 Oil	0.0	%	ISO 175
300% Strain，100℃，70 hr，in ASTM #3 Oil	8.0	%	ISO 175
100℃，168 hr，in ASTM #1 Oil	7.0	%	ISO 175
100% Strain，100℃，168 hr，in ASTM #1 Oil	-1.0	%	ISO 175
300% Strain，100℃，168 hr，in ASTM #1 Oil	7.0	%	ISO 175
100℃，168 hr，in ASTM #3 Oil	29	%	ISO 175
100% Strain，100℃，168 hr，in ASTM #3 Oil	-1.0	%	ISO 175
300% Strain，100℃，168 hr，in ASTM #3 Oil	4.0	%	ISO 175
100℃，336 hr，in ASTM #1 Oil	2.0	%	ISO 175
100% Strain，100℃，336 hr，in ASTM #1 Oil	-3.0	%	ISO 175
300% Strain，100℃，336 hr，in ASTM #1 Oil	-3.0	%	ISO 175
100℃，336 hr，in ASTM #3 Oil	32	%	ISO 175
100% Strain，100℃，336 hr，in ASTM #3 Oil	-2.0	%	ISO 175
300% Strain，100℃，336 hr，in ASTM #3 Oil	-2.0	%	ISO 175
100℃，504 hr，in ASTM #1 Oil	8.0	%	ISO 175
100% Strain，100℃，504 hr，in ASTM #1 Oil	-6.0	%	ISO 175
300% Strain，100℃，504 hr，in ASTM #1 Oil	-11	%	ISO 175
100℃，504 hr，in ASTM #3 Oil	20	%	ISO 175
100% Strain，100℃，504 hr，in ASTM #3 Oil	-8.0	%	ISO 175
300% Strain，100℃，504 hr，in ASTM #3 Oil	-11	%	ISO 175
Change rate of ultimate elongation			ASTM D471
23℃，70 hr，in Reference Fuel A（Isooctane）	0.0	%	ASTM D471
23 ℃, 70 hr, methanol	15	%	ASTM D471
23℃，168 hr，in Reference Fuel A（Isooctane）	0.0	%	ASTM D471
23 ℃, 168 hr, methanol	-17	%	ASTM D471
23℃，336 hr，in Reference Fuel A（Isooctane）	-7.0	%	ASTM D471
23℃，336 hr，in Reference Fuel C	12	%	ASTM D471
23℃，504 hr，in Reference Fuel A（Isooctane）	-1.0	%	ASTM D471
23℃，504 hr，in Reference Fuel C	10	%	ASTM D471
100 ℃, 70 hr, in ASTM # 1 oil	8.0	%	ASTM D471
100 ℃, 70 hr, in ASTM # 3 oil	4.0	%	ASTM D471
100℃，168 hr，in ASTM #1 Oil	-4.0	%	ASTM D471
100℃，168 hr，in ASTM #3 Oil	19	%	ASTM D471
100℃，336 hr，in ASTM #1 Oil	4.0	%	ASTM D471
100℃，336 hr，in ASTM #3 Oil	36	%	ASTM D471
100℃，504 hr，in ASTM #1 Oil	17	%	ASTM D471
100℃，504 hr，in ASTM #3 Oil	51	%	ASTM D471
Changes in tensile stress during fracture			ISO 175
23℃，70 hr，in Reference Fuel A（Isooctane）	0.0	%	ISO 175
23 ℃, 70 hr, methanol	15	%	ISO 175
23℃，168 hr，in Reference Fuel A（Isooctane）	0.0	%	ISO 175
23 ℃, 168 hr, methanol	-17	%	ISO 175
23℃，336 hr，in Reference Fuel A（Isooctane）	-7.0	%	ISO 175
23℃，336 hr，in Reference Fuel C	12	%	ISO 175
23℃，504 hr，in Reference Fuel A（Isooctane）	-1.0	%	ISO 175
23℃，504 hr，in Reference Fuel C	10	%	ISO 175
100 ℃, 70 hr, in ASTM # 1 oil	8.0	%	ISO 175
100 ℃, 70 hr, in ASTM # 3 oil	4.0	%	ISO 175
100℃，168 hr，in ASTM #1 Oil	-4.0	%	ISO 175
100℃，168 hr，in ASTM #3 Oil	19	%	ISO 175
100℃，336 hr，in ASTM #1 Oil	4.0	%	ISO 175
100℃，336 hr，in ASTM #3 Oil	36	%	ISO 175
100℃，504 hr，in ASTM #1 Oil	17	%	ISO 175
100℃，504 hr，in ASTM #3 Oil	51	%	ISO 175
The rate of change in Shore hardness			ASTM D471
Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane)	-1.0		ASTM D471
Shore D, 23°C, 70 hr, in Reference Fuel C	0.0		ASTM D471
Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane)	-5.0		ASTM D471
Shore D, 23 ℃, 168 hr, in reference fuel	-1.0		ASTM D471
Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane)	-1.0		ASTM D471
Shore D, 23 ℃, 336 hr, in reference fuel C	-4.0		ASTM D471
Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane)	2.0		ASTM D471
Shore D, 23 ℃, 504 hr, in reference fuel C	-5.0		ASTM D471
Shore D, 100°C, 70 hr, in ASTM #1 Oil	-1.0		ASTM D471
Shore D, 100 ℃, 70 hr, in ASTM # 3 oil	-4.0		ASTM D471
Shore D, 100°C, 168 hr, in ASTM #1 Oil	-3.0		ASTM D471
Shore D, 100 ℃, 168 hr, in ASTM # 3 oil	-5.0		ASTM D471
Shore D, 100 ℃, 336 hr, in ASTM # 1 oil	-4.0		ASTM D471
Shore D, 100 ℃, 336 hr, in ASTM # 3 oil	-2.0		ASTM D471
Shore D, 100 ℃, 504 hr, in ASTM # 1 oil	-2.0		ASTM D471
Shore D, 100 ℃, 504 hr, in ASTM # 3 oil	-5.0		ASTM D471
The rate of change in Shore hardness			ISO 175
Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane)	-1.0		ISO 175
Shore D, 23°C, 70 hr, in Reference Fuel C	0.0		ISO 175
Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane)	-5.0		ISO 175
Shore D, 23 ℃, 168 hr, in reference fuel	-1.0		ISO 175
Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane)	-1.0		ISO 175
Shore D, 23 ℃, 336 hr, in reference fuel C	-4.0		ISO 175
Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane)	2.0		ISO 175
Shore D, 23 ℃, 504 hr, in reference fuel C	-5.0		ISO 175
Shore D, 100°C, 70 hr, in ASTM #1 Oil	-1.0		ISO 175
Shore D, 100 ℃, 70 hr, in ASTM # 3 oil	-4.0		ISO 175
Shore D, 100°C, 168 hr, in ASTM #1 Oil	-3.0		ISO 175
Shore D, 100 ℃, 168 hr, in ASTM # 3 oil	-5.0		ISO 175
Shore D, 100 ℃, 336 hr, in ASTM # 1 oil	-4.0		ISO 175
Shore D, 100 ℃, 336 hr, in ASTM # 3 oil	-2.0		ISO 175
Shore D, 100 ℃, 504 hr, in ASTM # 1 oil	-2.0		ISO 175
Shore D, 100 ℃, 504 hr, in ASTM # 3 oil	-5.0		ISO 175
Volume change			ASTM D471
23℃，70 hr，in Reference Fuel A	0.0	%	ASTM D471
23 ℃, 70 hr, methanol	1.0	%	ASTM D471
23℃，168 hr，in Reference Fuel A	0.0	%	ASTM D471
23 ℃, 168 hr, methanol	2.0	%	ASTM D471
23℃，336 hr，in Reference Fuel A	0.0	%	ASTM D471
23℃，336 hr，in Reference Fuel C	2.0	%	ASTM D471
23℃，504 hr，in Reference Fuel A	0.0	%	ASTM D471
23℃，504 hr，in Reference Fuel C	2.0	%	ASTM D471
100 ℃, 70 hr, in ASTM # 1 oil	0.0	%	ASTM D471
100 ℃, 70 hr, in ASTM # 3 oil	0.0	%	ASTM D471
100℃，168 hr，in ASTM #1 Oil	0.0	%	ASTM D471
100℃，168 hr，in ASTM #3 Oil	1.0	%	ASTM D471
100℃，336 hr，in ASTM #1 Oil	0.0	%	ASTM D471
100℃，336 hr，in ASTM #3 Oil	2.0	%	ASTM D471
100℃，504 hr，in ASTM #1 Oil	0.0	%	ASTM D471
100℃，504 hr，in ASTM #3 Oil	2.0	%	ASTM D471
Volume change			ISO 175
23℃，70 hr，in Reference Fuel A	0.0	%	ISO 175
23 ℃, 70 hr, methanol	1.0	%	ISO 175
23℃，168 hr，in Reference Fuel A	0.0	%	ISO 175
23 ℃, 168 hr, methanol	2.0	%	ISO 175
23℃，336 hr，in Reference Fuel A	0.0	%	ISO 175
23℃，336 hr，in Reference Fuel C	2.0	%	ISO 175
23℃，504 hr，in Reference Fuel A	0.0	%	ISO 175
23℃，504 hr，in Reference Fuel C	2.0	%	ISO 175
100 ℃, 70 hr, in ASTM # 1 oil	0.0	%	ISO 175
100 ℃, 70 hr, in ASTM # 3 oil	0.0	%	ISO 175
100℃，168 hr，in ASTM #1 Oil	0.0	%	ISO 175
100℃，168 hr，in ASTM #3 Oil	1.0	%	ISO 175
100℃，336 hr，in ASTM #1 Oil	0.0	%	ISO 175
100℃，336 hr，in ASTM #3 Oil	2.0	%	ISO 175
100℃，504 hr，in ASTM #1 Oil	0.0	%	ISO 175
100℃，504 hr，in ASTM #3 Oil	2.0	%	ISO 175

Supplementary information	Nominal value	Unit	Test method
Compression load			ASTM D575
10% deflection	21.7	MPa	ASTM D575
15% deflection	25.9	MPa	ASTM D575
2% deflection	3.79	MPa	ASTM D575
20% deflection	29.3	MPa	ASTM D575
25% deflection	33.8	MPa	ASTM D575
5% deflection	13.1	MPa	ASTM D575
50% deflection	65.8	MPa	ASTM D575

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature – hot air dryer	100 to 110	°C
Drying time – hot air dryer	2.0	hr
Recommended maximum moisture content	< 0.030	%
Recommended injection volume	40 to 80	%
Proposed maximum recycled material ratio	20	%
Barrel rear temperature	210 to 235	°C
Barrel middle temperature	210 to 240	°C
Barrel front temperature	215 to 240	°C
Nozzle temperature	215 to 240	°C
Processing (melt) temperature	220 to 240	°C
Mold temperature	15 to 40	°C
Injection pressure	41.4 to 103	MPa
Injection speed	Slow-Moderate
Back pressure	< 1.38	MPa
Screw speed	40 to 80	rpm
Clamping force	4.1 to 6.9	kN/cm²
Cushion	< 3.18	mm
Screw length to diameter ratio	20.0:1.0
Screw compression ratio	2.5:1.0 to 3.0:1.0

Notes
1. Typical properties: these are not to be construed as specifications.
2. Die C
3. Post-cured 16 hr at 230°F
4. Rate A (50°C/h)
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.