| About |
|---|
| Lead-free Thermoplastic CPE compound THERMODAN®CP 0110-108 BK is a black, UV resistant, lead-free, RoHS compliant, thermoplastic CPE compound. It is designed for use in a wide variety of jacketing applications including wire and cable and tube bundles. This compound has superior fire performance, including slow flame propagation, and self-extinguishing characteristics. THERMODAN® CP 0110-108 BK should be extruded with a screw configuration designed to optimize process conditions and throughput. This extrusion compound meets, or exceeds, several industry jacketing specifications, including UL 1277 tray cable.&& |
| Product Description | |
|---|---|
| Generic | CPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Self-extinguishing,Lead content is low to none |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 6.0 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | |||
| cracking | 67 | kN/m | ASTM D470 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength | |||
| 75℃，1440 hr，in Oil | 80 | % | |
| 100℃，96 hr，in Oil | 65 | % | |
| 121℃，168 hr | 95 | % | |
| Change rate of ultimate elongation | |||
| 75 ℃, 1440 hr, in oil | 75 | % | |
| 100 ℃, 96 hr, in oil | 70 | % | |
| 121℃，168 hr | 110 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -19.0 | ℃ | ASTM D746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 37 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 1 second | 93 | ||
| Shore D, 10 seconds | 60 | ||
| tensile strength | |||
| fracture | 15.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 350 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 110 | MPa | ASTM D790 |
| Load deformation | |||
| 100℃，0.20 MPa | 12.0 | % | |
| 121℃，0.20 MPa | 24.0 | % |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 149 to 160 | °C | |
| Barrel 2 zone temperature | 160 to 174 | °C | |
| Barrel 3 zone temperature | 174 to 185 | °C | |
| Barrel 4 zone temperature | 174 to 185 | °C | |
| Barrel 5 zone temperature | 174 to 185 | °C | |
| Melt temperature | 182 to 193 | °C | |
| Nozzle temperature | 188 to 199 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 3min in methanol |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |