| About |
|---|
| The FR Series is your material solution for applications requiring high flame retardance. The compounds are halogen free and available in natural and black colors. Typical applications Cable holders Seals for in-wall outlets Seals for plugs Seals for switch boxes Material advantages Easy coloring (compounds in natural colors) Excellent mechanical properties Halogen free (reduction of toxic fire gases) Self-extinguishing, no dripping of flaming particles UL 94-V0 (3mm) listed&& |
| Product Description | |
|---|---|
| Supplier | KRAIBURG |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Self-extinguishing,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 2.00 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 500 | % | ISO 37 |
| tear strength | 13 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，72 hr | 8.0 | % | ISO 815 |
| 70℃，24 hr | 29 | % | ISO 815 |
| 100℃，24 hr | 83 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 37 | ISO 7619 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 160 | °C | |
| Barrel 2 zone temperature | 190 | °C | |
| Barrel 3 zone temperature | 220 | °C | |
| Nozzle temperature | 180 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type S2, 7.9 in/min |
| 3. Method Bb, Angle (Nicked) |
| 4. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |