| About |
|---|
| The MC/tl Series is your material solution for applications requiring basic medical approvals such as ISO 10993-5. The compounds are produced exclusively by a special medical unit and available in translucent colors. Typical applications Flexible Connections Mouthpieces Seals Soft touch Valves Material advantages Adhesion to PP DMF listed Excellent compression set For injection molding and extrusion Free of animal basedingredients KRAIBURG TPE Medical service package (description below) Sterilizable (autoclave 134°C, gammaradiation 2×35 kGy, EtO) Tested according to ISO 10993-5&& |
| Product Description | |
|---|---|
| Supplier | KRAIBURG |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | ADCF,High pressure disinfection,Good bond,Radiation disinfection,Ethylene oxide disinfection |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 68 | ISO 7619 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 13.0 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 800 | % | ISO 37 |
| tear strength | 24 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，72 hr | 30 | % | |
| 70℃，24 hr | 38 | % | |
| 100℃，24 hr | 55 | % |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60.0 to 80.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 160 | °C | |
| Barrel 2 zone temperature | 180 | °C | |
| Barrel 3 zone temperature | 200 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type S2, 7.9 in/min |
| 3. Method Bb, Angle (Nicked) |
| 4. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |