| About |
|---|
| The LTP/PA Series is your material solution for sealings requiring high temperature resistance.The compounds are characterized by an excellent adhesion to PA. Typical applications Fastenings Grommets Seals Material advantages Adhesion to PA6 and PA6.6 up to 50 % glass fiber Excellent heat stability Exceptional long-term compression set&& |
| Product Description | |
|---|---|
| Supplier | KRAIBURG |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Good bond,Heat Stabilized |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 80 | ISO 7619 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 12.0 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 550 | % | ISO 37 |
| tear strength | 25 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，72 hr | 35 | % | ISO 815 |
| 70℃，24 hr | 45 | % | ISO 815 |
| 120℃，24 hr | 70 | % | ISO 815 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesion to PA6（A） | 6.0 | kN/m | VDI 2019 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 230 to 245 | °C | |
| Barrel middle temperature | 250 to 260 | °C | |
| Barrel front temperature | 260 to 270 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Injection pressure | 2.00 to 100 | MPa | |
| Back pressure | 2.00 to 10.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type S2, 7.9 in/min |
| 3. Method Bb, Angle (Nicked) |
| 4. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |