| About |
|---|
| Thermoset Plastics 351是一种环氧; 环氧树脂材料,含有的填充物为填料。 该产品在北美洲有供货,加工方式为:包封或浇铸。 Thermoset Plastics 351的主要特性有: 绝缘 耐热 良好的柔韧性 Thermoset Plastics 351的典型应用领域为:电线电缆&& |
| Product Description | |
|---|---|
| Supplier | Lord |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good thermal shock resistance,Insulation |
| Availabilitys | North America |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 110 | J/m | ASTM D256 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+15 | ohms·cm | ASTM D257 |
| Dielectric constant | |||
| 1 MHz | 4.30 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.028 | ASTM D150 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| resin | 按重量计算的混合比: 2.0 | ||
| Hardening method | 按重量计算的混合比: 3.0 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 45000 | cP | ASTM D2393 |
| stripping time | |||
| 121℃ | 120 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 65 | ASTM D2240 | |
| tensile strength | |||
| yield | 15.2 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 45 | % | ASTM D638 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |