TIPELIN 7300B is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blow moulding of products with high stiffness and excellent environmental stress crack resistance (ESCR).The grade contains antioxidant and acid scavenger. Applications TIPELIN 7300B is recommended for blow moulding of jerry cans for packaging of aggressive industrial chemicals bounded to UN certificates. The grade is recommended for sheet extrusion as well. It is suitable for corrugated pipes too. TIPELIN 7300B is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact and Pharmaceutical Regulations.&&

About

TIPELIN 7300B is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blow moulding of products with high stiffness and excellent environmental stress crack resistance (ESCR).The grade contains antioxidant and acid scavenger. Applications TIPELIN 7300B is recommended for blow moulding of jerry cans for packaging of aggressive industrial chemicals bounded to UN certificates. The grade is recommended for sheet extrusion as well. It is suitable for corrugated pipes too. TIPELIN 7300B is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact and Pharmaceutical Regulations.&&

Product Description
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Renewable resources,Food contact compliance,Inoxidizability,Butylene copolymer,Solvent resistance,High ESCR
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.955	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.10	g/10min	ISO 1133
190℃，21.6kg	12	g/10min	ISO 1133
190℃，5.0kg	0.40	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
10% non-ionic detergent, F50	1000	hr	ASTM D1693B

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	64		ISO 868
tensile strength
Fracture, molded	36.0	MPa	ISO 527-2
Yield, molding	37.0	MPa	ISO 527-2
Tensile strain
Fracture, molded	1400	%	ISO 527-2
Yield, molding	12	%	ISO 527-2
Bending modulus	1600	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	18	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	127	℃	ISO 306/A120
Oxygen sensing time
200℃	40	min	EN 728

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	180 to 220	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.