| About |
|---|
| TIPELIN FS 471-02 is a film grade of high density polyethylene copolymer (with hexene-1 as comonomer) grade. The product has high molecular mass, very good Tear strength and Dart drop resistance, low gel content, good vapour barrier properties. The grade contains antioxidant and acid scavenger. Applications TIPELIN FS 471-02 is recommended for extra thin packaging films, bags, shopping bags and garbage bags. TIPELIN FS 471-02 is suitable for food contact. The product complies with Food Contact Regulations.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Renewable resources,Low speed solidification point,Food contact compliance,Moisture resistance,Inoxidizability,High molecular weight,Good tear strength,Hexene copolymers |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.946 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.18 | g/10min | ISO 1133 |
| 190℃，21.6kg | 15 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.80 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ISO 868 | |
| Bending modulus | 1200 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 25.0 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 23.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, 25 µ m, blow molded film | 53.0 | MPa | ISO 527-3 |
| TD, 25 µ m, blow molded film | 47.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 700 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 800 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 95 | g | ISO 7765-1/A |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 25 µ m, blow molded film | 0.23 | N | ISO 6383-2 |
| TD: 25 µ m, blow molded film | 2.7 | N | ISO 6383-2 |
| Spencer Impact | |||
| Blow molded film, 25.0 µ m | 35.0 | MPa | ASTM D3420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 125 | ℃ | ISO 306/A120 |
| Oxygen sensing time | |||
| 200℃ | 70 | min | EN 728 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |