Tipwood® 50 EX

About
Tipwood® 50 EX is a Wood-Fibre Reinforced, Heat Stabilized Polypropylene Compound specially developed by Tipco for Automobile Interiors and Appliance Fascia Applications Features: Environmentally Friendly Material Easy Recyclability 45-50% Special Wood Filler Excellent Extrudability High Melt Strength Superior Draw Down for Vacuum / Thermo Formability Wood-Like Surface Aesthetics Good Izod Impact Strength High Stiffness & Good Durability Good Sound Barrier Properties Extremely Low Thermal Sag Applications: Sheet Extrusion, Thermoforming, Profiles, Blow Moulding and Lamination. Automotive Car Interiors, Door Panels, Trims, Wood-Finish Panels, Office Files, Trays, Marine Flooring, Audio Speakers, Resonator Devices, Blow Moulded Bottles, Furniture, Mono-Block Chairs and various Artificial Wood Products.&&

About

Tipwood® 50 EX is a Wood-Fibre Reinforced, Heat Stabilized Polypropylene Compound specially developed by Tipco for Automobile Interiors and Appliance Fascia Applications Features: Environmentally Friendly Material Easy Recyclability 45-50% Special Wood Filler Excellent Extrudability High Melt Strength Superior Draw Down for Vacuum / Thermo Formability Wood-Like Surface Aesthetics Good Izod Impact Strength High Stiffness & Good Durability Good Sound Barrier Properties Extremely Low Thermal Sag Applications: Sheet Extrusion, Thermoforming, Profiles, Blow Moulding and Lamination. Automotive Car Interiors, Door Panels, Trims, Wood-Finish Panels, Office Files, Trays, Marine Flooring, Audio Speakers, Resonator Devices, Blow Moulded Bottles, Furniture, Mono-Block Chairs and various Artificial Wood Products.&&

Product Description
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,noise reduction,Good melt strength,Copolymer,Durability
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.08	g/cm³	ASTM D1505
Melt Flow Rate
230℃，10.0kg	6.0	g/10min	ASTM D1238
Shrinkage rate
MD	0.80	%	ASTM D955
water content	0.25	%	ASTM D817

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	24.5	MPa	ASTM D638
Tensile strain
fracture	8.0	%	ASTM D638
Bending modulus	2450	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	34	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	92.0	℃	ASTM D648

Process Conditions
Extrusion	Nominal value	Unit	Test method
Drying temperature	80 to 90	°C
Drying time	5.0 to 7.0	hr
Melt temperature	< 225	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.