| About |
|---|
| Tislamid® PA66 PA66 15 GFR是一种聚酰胺66（尼龙66）材料,含有的填充物为15% 玻璃纤维增强材料。 该产品在非洲和中东或欧洲有供货,加工方式为:注射成型。 Tislamid® PA66 PA66 15 GFR的主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.40 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.3 | % | ISO 62 |
| Ash Content | 15 | % | ISO 3451 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 248 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| B120 | 250 | ℃ | ISO 306/B120 |
| Melting temperature | 260 to 265 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| 3.00 mm | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 650 | ℃ | IEC 60695-2-12 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 84 | ISO 868 | |
| tensile strength | ISO 527-2 | ||
| yield | 125 | MPa | ISO 527-2 |
| fracture | 125 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 3.0 | % | ISO 527-2 |
| fracture | 3.0 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 260 to 280 | °C | |
| Barrel front temperature | 260 to 280 | °C | |
| Nozzle temperature | 250 to 270 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 75 to 85 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |