| Titacon® TX910是一种聚甲醛（POM）共聚物材料,。 该产品在亚太地区有供货,。 Titacon® TX910的主要特性有: 阻燃/额定火焰 冲击改性 良好的韧性&& |
| Product Description | |
|---|---|
| Supplier | Titan |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Moderate liquidity,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| 3.0 mm | 1.7 to 2.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 45 | % | ISO 527-2 |
| Bending modulus | 1700 | MPa | ISO 178 |
| bending strength | 65.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 14 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 87.0 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 170 to 200 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |