Titalon® 2150TF N180

About

Product Description
Supplier	Titan
Generic	PA66
Material Status	Commercial: Active
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.26	g/cm³	ISO 1183
Shrinkage rate
3.0 mm	0.30 to 0.70	%

MECHANICAL	Nominal value	Unit	Test method
tensile strength	125	MPa	ISO 527-1,2
Tensile strain
fracture	>3.0	%	ISO 527-1,2
Bending modulus	5400	MPa	ISO 178
bending strength	190	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	14	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	235	℃	ISO 75-1,2

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+14	ohms	IEC 60093
Volume resistivity	1.0E+13	ohms·cm	IEC 60093

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	80 to 100	°C
Drying time	4.0	hr
Processing (melt) temperature	260 to 290	°C
Mold temperature	60 to 100	°C
Injection Pressure	30-70	%
injection speed	30-60	%

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.