| About |
|---|
| Titalon® 2300CF is a Polyamide 66 (Nylon 66) material filled with 30% carbon fiber. It is available in Asia Pacific. Important attributes of Titalon® 2300CF are: Flame Rated Conductive Wear Resistant&& |
| Product Description | |
|---|---|
| Supplier | Titan |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Conductive,Good wear resistance,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| 3.0 mm | 0.20 to 0.60 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 240 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 1.0 | % | ISO 527-2 |
| Bending modulus | 19000 | MPa | ISO 178 |
| bending strength | 350 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 | ohms | IEC 60093 |
| Volume resistivity | 10 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50x70x3 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |