| Titan® 9200GF是一种聚醚酰亚胺(PEI)材料,含有的填充物为10% 玻璃纤维增强材料。 该产品在亚太地区有供货,。 Titan® 9200GF的主要特性为:阻燃/额定火焰。 |
| Product Description | |
|---|---|
| Supplier | Titan |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| 3.0 mm | 0.30 to 0.60 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile stress | 120 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 3.0 | % | ISO 527-2 |
| Bending modulus | 5000 | MPa | ISO 178 |
| Bending stress | 180 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 206 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 140 to 150 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 350 to 390 | °C | |
| Mold temperature | 130 to 180 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |