| About |
|---|
| Polypropylene homopolymer. The base resin meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520(a)(1)(i) and (c)1.1a. The adjuvant meet their respective FDA regulations and 21 CFR 177.1520(b). In summary, this resin meets the FDA criteria covering safe use of polyolefin articles and component of articles intended for food contact use. TSCA Registry: CAS# 9003-07-0 APPLICATIONS: Slit tape and monofilament for rope, twine, yarn and industrial fabrics and thermoformed articles. Characteristics: Outstanding processability, maximum bubble stability for slit tape production by the tubular process, good melt stability and superior fiber strength, low color, low taste & odor, no plate-out problems on die lips or chill rolls and good heat-aging stability in yarn and fabric. FABRICATION: Equipment – general extrusion and techniques – standard processing for tubular and flat die tapes.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good heat aging resistance,Food contact compliance,Low odor,Good sensory characteristics.,Homopolymer,Higher melt stability |
| Availabilitys | Asia Pacific |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.7 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 24hr | 0.020 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 54 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95.0 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 95 | ASTM D785 | |
| tensile strength | |||
| yield | 35.3 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 12 | % | ASTM D638 |
| Bending modulus | 1720 | MPa | ASTM D790B |
| Notes |
|---|
| 1. CAS# 9003-07-0 |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |