| 10% Deflection for optimum life Hardness 60 Shore D High abrasion and wear resistance Good machinability High loadbearing capacity Special forming applications.&& |
| Product Description | |
|---|---|
| Generic | PUR |
| Material Status | Commercial: Active |
| Features | Machinable,Good wear resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | |
| Shrinkage rate | |||
| MD | 1.7 | % | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Graves Tear | 148.9 | kN/m |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 100% strain | 17.2 | MPa | |
| 300% strain | 46.2 | MPa | |
| tensile strength | 50.0 | MPa | |
| Tensile strain | |||
| fracture | 350 | % | |
| tear strength | |||
| cracking | 22 | kN/m | ASTM D470 |
| Compression deformation | |||
| 70℃，22 hr | 42 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -67.8 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Bayshore Resistance（NBS Index） | 55.0 | ||
| Penetration depth | |||
| Recommended for optimum life | 10 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 98 | ||
| Shaw’s D | 62 | ||
| friction coefficient | |||
| Steel – Dynamic | 0.30 | ||
| abrasion resistance | |||
| NBS Index | 375 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. at 20 lbs load at 52 fpm |
| 3. Method B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |