| TOPAS® 6013L-17是一种环烯烃共聚物 (COC)产品,。 它,在亚太地区有供货。 典型应用领域为:光学/镜头。 特性包括: 阻燃/额定火焰 共聚物&& |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | COC |
| Material Status | Commercial: Active |
| Features | Copolymer |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 0.01 | % | ISO 62 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 14 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 63 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.8 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 2900 | MPa | ISO 527-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.53 | ISO 489 | |
| Transmittance | |||
| 2000 μm | 91 | % | ISO 13468-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 130 | ℃ | ISO 75-2/Bf |
| Glass transition temperature | 140 | ℃ | ISO 11357-2 |
| Vicat Softening Temp |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | HB | UL-94 | |
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 2.0 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |