| TOPAS® 6015S-04 Product Description TOPAS 6015S-04 is a general purpose injection molding grade. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for optics, healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve food and drug stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. This grade has a high (150°C) heat distortion temperature to withstand 121°C and 134°C steam and dry heat sterilization protocols, as well as gamma and EtO procedures. Selected Applications Drug delivery Prefilled syringes, vials, cartridges Bottles and tubes Surgical instruments IV containers and components Labware Optics Electronics Food packaging Healthcare and food contact Leading Attributes Low leachables & extractables, low water transmission Non-ionic, does not promote adsorption like glass Minimally reactive Chemically resistant to alcohol, acetone, and acrylates Transparent, withstands EtO/gamma/steam sterilization Temperature resistance, clarity and purity Clarity, low birefringence, low moisture sensitivity Low dielectric constant, thermoplastic Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Injection Molding, Healthcare, Optics and Diagnostics TOPAS 6013M-07 – broader processing window, best for blow molding (IBM/ISBM) TOPAS 6017S-04 – our most heat distortion resistant IM grade (HDT=170°C)&&TOPAS® 6015S-04 TOPAS® 6015S-04 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Characteristics include: Flame Rated Copolymer&& |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | COC |
| Material Status | Commercial: Active |
| Features | Good Clarity,Low extract,High purity,Steam sterilized,Halogen free,Food contact compliance,High Heat Resistance,Moisture resistance,No BPA,Radiation disinfection,Copolymer,Solvent resistance,Ethylene oxide disinfection,Heat sterilization,Amorphous,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 3.7 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 4.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.010 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 60.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 2.5 | % | ISO 527-2/1A/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 1.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 150 | ℃ | ISO 75-2/B |
| Glass transition temperature | 158 | ℃ | ISO 11357-2 |
| Vicat Softening Temp | |||
| B50 | 156 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Relative permittivity | IEC 60250 | ||
| 1 kHz | 2.35 | IEC 60250 | |
| 10 kHz | 2.35 | IEC 60250 | |
| Dissipation factor | |||
| 1 GHz | 7.0E-5 | IEC 60250 | |
| Compared to the leakage tracing index | > 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.530 | ISO 489 | |
| Transmittance | 91.0 | % | ISO 13468-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Injection speed | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 240 to 270 | °C | |
| Barrel middle temperature | 250 to 310 | °C | |
| Barrel front temperature | 260 to 310 | °C | |
| Nozzle temperature | 250 to 310 | °C | |
| Processing (melt) temperature | 260 to 310 | °C | |
| Mold temperature | 110 to 145 | °C | |
| Injection pressure | 50.0 to 110 | MPa | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Back pressure | < 15.2 | MPa | |
| Screw speed | 50 to 200 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Dependent on processing conditions and part design. |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |