TOPAS® 8007F-04

About
TOPAS® 8007F-04 Product Description TOPAS 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer cast applications, and in coextrusions in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as blister, twist, barrier, shrink and easy tear packaging. Industrial uses include formed decorative sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Pharmaceutical blisters Deep draw barrier trays Shrink films and labels Twist films Decorative sheet Food packaging Food contact Leading Attributes Clarity, forming, barrier, purity, halogen-free Excellent deep forming, unlike other barriers High shrink, low stress, gloss, clarity, toughness High gloss, outstanding deadfold, clean cutting Gloss, hardness, chemical resistance, forming Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 8007F-600 – robust clarity extrusion grade especially for PE blends&&TOPAS® 8007F-04 TOPAS® 8007F-04 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Primary characteristic: copolymer.&&

About

TOPAS® 8007F-04 Product Description TOPAS 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer cast applications, and in coextrusions in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as blister, twist, barrier, shrink and easy tear packaging. Industrial uses include formed decorative sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Pharmaceutical blisters Deep draw barrier trays Shrink films and labels Twist films Decorative sheet Food packaging Food contact Leading Attributes Clarity, forming, barrier, purity, halogen-free Excellent deep forming, unlike other barriers High shrink, low stress, gloss, clarity, toughness High gloss, outstanding deadfold, clean cutting Gloss, hardness, chemical resistance, forming Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 8007F-600 – robust clarity extrusion grade especially for PE blends&&TOPAS® 8007F-04 TOPAS® 8007F-04 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Primary characteristic: copolymer.&&

Product Description
Supplier	Polyplastics
Generic	COC
Material Status	Commercial: Active
Features	Good Rigidity,Good Clarity,Good flexibility,High purity,Good surface appearance,Halogen free,Food contact compliance,Moisture resistance,No BPA,Copolymer,Solvent resistance,Amorphous
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Film extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.02	g/cm³	ISO 1183
Water absorption rate
23℃，24hr	0.01	%	ISO 62
Melt Flow Rate
190℃，2.16kg	1.8	g/10min	ISO 1133
230℃，2.16kg	11	g/10min	ISO 1133
water vapor permeability	3.70	g mil/ (m2 day
Oxygen permeation	997	cm3 mil/(m2 day atm
Water vapor penetration rate	0.0008	g/m²/day	ISO 15106-3
thickness	70	g/min

MECHANICAL	Nominal value	Unit	Test method
Tensile strain
MD, fracture, 23 ℃	2.9	%	ISO 527-2
TD, fracture, 23 ℃	3	%	ISO 527-2
Drop test	<=36	g	ISO 7765-1
Elmendorf tear strength	225	g	ISO 6383-2
Elmendorf tear strength	230	g	ISO 6383-2
tensile strength
tensile strength
Tensile modulus
TD，23℃	1800	MPa	ISO 527-2
MD，23℃	2200	MPa	ISO 527-2
fracture	50	MPa	ISO 527-3
fracture	57	MPa	ISO 527-3

optical performance	Nominal value	Unit	Test method
Haze μ M	<=0.1	%	ISO 13468-2
gloss	>=100	%	ISO 2813

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	78	℃	ISO 11357-2
Vicat Softening Temp

Notes
1. Typical properties: these are not to be construed as specifications.
2. 90% RH
3. 10°C/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.