| About |
|---|
| TOPAS® 8007F-600 Product Description TOPAS 8007F-600 is a new robust film extrusion grade designed for blending with polyethylene (PE). It is an improved clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Forming films (header bags, etc.) Protective packaging Shrink films and labels Twist films Decorative sheet Food packaging Food contact Leading Attributes Clarity, forming, barrier, purity, halogen-free Stiffness for downgauging, improved forming High shrink, low stress, gloss, toughness Outstanding deadfold, clean cutting Stiffness, chemical resistance, forming, even draw Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 8007F-04 – ultimate clarity extrusion grade&&TOPAS® 8007F-600 TOPAS® 8007F-600 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Primary characteristic: copolymer.&& |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | COC |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High purity,Good surface appearance,Halogen free,Food contact compliance,Moisture resistance,No BPA,Copolymer,Solvent resistance,High shrinkage,Amorphous |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 1.8 | g/10min | ISO 1133 |
| 230℃，2.16kg | 10 | g/10min | ISO 1133 |
| Melt Volume Rate | ISO 1133 | ||
| 190℃，2.16 kg | 2.00 | cm³/10min | ISO 1133 |
| 230℃，2.16 kg | 11.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.010 | % | ISO 62 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 70 | µm | |
| Tensile modulus | ISO 527-3/1 | ||
| MD, 70 µ m, cast thin film | 2100 | MPa | ISO 527-3/1 |
| TD, 70 µ m, cast thin film | 1700 | MPa | ISO 527-3/1 |
| tensile strength | ISO 527-3/50 | ||
| MD, fracture, 70 µ m, blow molded film | 55.0 | MPa | ISO 527-3/50 |
| TD, fracture, 70 µ m, blow molded film | 50.0 | MPa | ISO 527-3/50 |
| Tensile strain | ISO 527-3/50 | ||
| MD, fracture, 70 µ m, cast thin film | 3.4 | % | ISO 527-3/50 |
| TD, fracture, 70 µ m, cast thin film | 3.4 | % | ISO 527-3/50 |
| Water vapor transmittance | |||
| 70 µ m, 23 ℃, cast film, 85% RH | 0.10 | g·mm/m²/atm/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 78.0 | ℃ | ISO 11357-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, 70.0 µ m, cast thin film | > 100 | ISO 2813 | |
| Haze | |||
| 70.0 µ m, cast thin film | > 2.0 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extruder screw length to diameter ratio L / D | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Extruder feed section | 20 to 60 | °C | |
| Barrel 1 zone temperature | 200 to 210 | °C | |
| Barrel 2 zone temperature | 200 to 210 | °C | |
| Barrel 3 zone temperature | 200 to 210 | °C | |
| Barrel 4 zone temperature | 200 to 210 | °C | |
| Nozzle temperature | 220 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 90% RH |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |