| About |
|---|
| TOPAS® 9506F-04 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Primary characteristic: copolymer.&& |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | COC |
| Material Status | Commercial: Active |
| Features | Copolymer |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Volume Rate | ISO 1133 | ||
| 190℃，2.16 kg | 1.00 | cm³/10min | ISO 1133 |
| 230℃，2.16 kg | 6.00 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.010 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2600 | MPa | ISO 527-2/1A/1000 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-3 | ||
| MD | 1700 | MPa | ISO 527-3 |
| TD | 2000 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture | 55.0 | MPa | ISO 527-3 |
| TD, fracture | 55.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture | 2.9 | % | ISO 527-3 |
| TD, fracture | 3.6 | % | ISO 527-3 |
| Drop hammer impact | < 36 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD | 2.3 | N | ISO 6383-2 |
| TD | 2.4 | N | ISO 6383-2 |
| Oxygen permeability | |||
| 23℃，50% RH | 17 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| water vapor permeability | |||
| 38℃ | 0.800 | g·100µm/(m²·day | ISO 15106-3 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 65.0 | ℃ | ISO 11357-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | > 100 | ISO 2813 | |
| Haze | < 1.0 | % | ISO 14782 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 90% RH |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |